| Tsis muaj. | Resin Khoom | Yam nqi | Chav tsev | Txoj Kev Xeem |
| 1 | Lub ntiajteb txawj nqus, 23 ℃ | 1.05 Nws | g/cm³ | ASTM D 792 Cov Lus Qhia Tshwj Xeeb |
| 2 | Pwm Shrinkage, 23 ℃, 3.2mm, 23 ℃ | 0.4-0.7 hli | % | ASTM D 955 Cov Lus Qhia Tshwj Xeeb |
| 3 | Melt Flow Rate, 220 ℃, 10kg | 22 | g/10 min | ASTM D 1238 Cov |
| 4 | Tensile Strength ntawm Yield, 23 ℃, 50mm / min, 3.2mm | 49 | MPa | ASTM D 638 Cov |
| 5 | Tensile Elongation ntawm Yield, 23 ℃, 50mm / min, 3.2mm | 5 | %, (Min) | ASTM D 638 Cov |
| 6 | Tensile Elongation ntawm tawg, 23' ℃, 50mm / min, 3.2mm | 10 | %, (Min) | ASTM D 638 Cov |
| 7 | Tensile Modulus, 23 ℃, 50mm / min, 3.2mm | 2350 | MPa | ASTM D 638 Cov |
| 8 | Flexural zog, 23 ℃, 15mm / min, 3.2mm | 78 | MPa | ASTM D 790 Cov Lus Qhia Tshwj Xeeb |
| 9 | Flexural Modulus, 23 ℃, 15mm / min, 3.2mm | 2550 | MPa | ASTM D 790 Cov Lus Qhia Tshwj Xeeb |
| 10 | Izod Impact Strength, Notched, 3.2mm, 23 ℃ | 220 | J/m | ASTM D256 |
| 11 | Izod Impact Strength, Notched, 3.2mm, -30 ℃ | 90 | J/m | ASTM D256 |
| 12 | Izod Impact Strength, Notched, 6.4mm, 23 ℃ | 220 | J/m | ASTM D256 |
| 13 | Izod Impact Strength, Notched, 6.4mm, -30 ℃ | 90 | J/m | ASTM D256 |
| 14 | Rockwell Hardness, R-Scale | 110 | / | ASTM D 785 Cov Lus Qhia Tshwj Xeeb |
| 15 | HDT, Edgewise, 1.82MPa, 6.4mm, Unannealed | 85 | °C | ASTM D 648 3 |
| 16 | VICAT, 50N, 50 ℃ / h | 92 | °C | ASTM D 1525 Cov Lus Qhia |
| 17 | RTI hluav taws xob | 95 | °C | SIB 746B |
| 18 | RTI Mechanical nrog Impact | 95 | °C | SIB 746B |
| 19 | RTI Mechanical tsis cuam tshuam | 95 | °C | SIB 746B |
| 20 | Flammability, 1.5 hli | HB | / | UAS 94 |
| 21 | Flammability, 3.0 hli | HB | / | UAS 94 |